We report a one-step synthesis protocol for obtaining polymer-coated magnetic nanoparticles (MNPs) engineered for uploading neural cells. Polyethyleneimine-coated Fe3O4 nanoparticles (PEI-MNPs) with sizes of 25 ± 5 nm were prepared by oxidation of Fe(OH)2 by nitrate in basic aqueous media and adding PEI in situ during synthesis. The obtained PEI-MNP cores displayed a neat octahedral morphology and high crystallinity. The resulting nanoparticles were coated with a thin polymer layer of about 0.7-0.9 nm, and displayed a saturation magnetization value M S = 58 A m2 kg-1 at 250 K (64 A m2 kg-1 for T = 10 K). Cell uptake experiments on a neuroblastoma- derived SH-SY5Y cell line were undertaken over a wide time and MNP concentration range. The results showed a small decrease in cell viability for 24 h incubation (down to 70% viability for 100 μg ml-1), increasing the toxic effects with incubation time (30% cell survival at 100 μg ml -1 for 7 days of incubation). On the other hand, primary neuronal cells displayed higher sensitivity to PEI-MNPs, with a cell viability reduction of 44% of the control cells after 3 days of incubation with 50 μg ml -1. The amount of PEI-MNPs uploaded by SH-SY5Y cells was found to have a linear dependence on concentration. The intracellular distribution of the PEI-MNPs analyzed at the single-cell level by the dual-beam (FIB/SEM) technique revealed the coexistence of both fully incorporated PEI-MNPs and partially internalized PEI-MNP-clusters crossing the cell membrane. The resulting MNP-cluster distributions open the possibility of using these PEI-MNPs for magnetically driven axonal re-growth in neural cells.
Neuronal cells loaded with PEI-coated Fe3O4 nanoparticles for magnetically guided nerve regeneration
RIGGIO, CRISTINA;RAFFA, VITTORIA;
2013-01-01
Abstract
We report a one-step synthesis protocol for obtaining polymer-coated magnetic nanoparticles (MNPs) engineered for uploading neural cells. Polyethyleneimine-coated Fe3O4 nanoparticles (PEI-MNPs) with sizes of 25 ± 5 nm were prepared by oxidation of Fe(OH)2 by nitrate in basic aqueous media and adding PEI in situ during synthesis. The obtained PEI-MNP cores displayed a neat octahedral morphology and high crystallinity. The resulting nanoparticles were coated with a thin polymer layer of about 0.7-0.9 nm, and displayed a saturation magnetization value M S = 58 A m2 kg-1 at 250 K (64 A m2 kg-1 for T = 10 K). Cell uptake experiments on a neuroblastoma- derived SH-SY5Y cell line were undertaken over a wide time and MNP concentration range. The results showed a small decrease in cell viability for 24 h incubation (down to 70% viability for 100 μg ml-1), increasing the toxic effects with incubation time (30% cell survival at 100 μg ml -1 for 7 days of incubation). On the other hand, primary neuronal cells displayed higher sensitivity to PEI-MNPs, with a cell viability reduction of 44% of the control cells after 3 days of incubation with 50 μg ml -1. The amount of PEI-MNPs uploaded by SH-SY5Y cells was found to have a linear dependence on concentration. The intracellular distribution of the PEI-MNPs analyzed at the single-cell level by the dual-beam (FIB/SEM) technique revealed the coexistence of both fully incorporated PEI-MNPs and partially internalized PEI-MNP-clusters crossing the cell membrane. The resulting MNP-cluster distributions open the possibility of using these PEI-MNPs for magnetically driven axonal re-growth in neural cells.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.