In this paper, we investigate Er3+-doped monocrystalline BaY2F8 as an upconverter material for crystalline silicon solar cells with the aim of making use of previously not-utilized sub-bandgap photons. Monocrystalline samples with 10%, 20% and 30% Er3+ doping were grown in a Czochralski furnace and subsequently attached to an adapted planar bifacial silicon solar cell with a 33.4 mA/cm2 short-circuit current density under one-sun AM1.5G standard measurement conditions. Optical characterization revealed that for the investigated illumination conditions the 30% Er3+-doped samples showed the most promising properties, with a very high peak absorption coefficient of 45.1 cm−1 at 1493 nm and a high external (internal) upconversion quantum yield of 9.5±0.7% (10.1±1.6%) under 4740±250 W m−2 monochromatic irradiation at 1520 nm. Solar simulator measurements of the upconverter solar cell device using the BaY2F8:30% Er3+ sample showed an additional short-circuit current density due to upconversion ΔjSC,UC of 17.2±3.0 mA/cm2 at an illumination with a solar concentration of 94±17 suns, equivalent to a record relative enhancement of the short-circuit current of 0.55±0.14%. This value constitutes to our knowledge more than a doubling compared to the previously highest published values and more than a 35-fold increase compared to values published three years ago.

Record efficient upconverter solar cell devices with optimized bifacial silicon solar cells and monocrystalline BaY2F8:30% Er3+ upconverter

TONELLI, MAURO;
2015-01-01

Abstract

In this paper, we investigate Er3+-doped monocrystalline BaY2F8 as an upconverter material for crystalline silicon solar cells with the aim of making use of previously not-utilized sub-bandgap photons. Monocrystalline samples with 10%, 20% and 30% Er3+ doping were grown in a Czochralski furnace and subsequently attached to an adapted planar bifacial silicon solar cell with a 33.4 mA/cm2 short-circuit current density under one-sun AM1.5G standard measurement conditions. Optical characterization revealed that for the investigated illumination conditions the 30% Er3+-doped samples showed the most promising properties, with a very high peak absorption coefficient of 45.1 cm−1 at 1493 nm and a high external (internal) upconversion quantum yield of 9.5±0.7% (10.1±1.6%) under 4740±250 W m−2 monochromatic irradiation at 1520 nm. Solar simulator measurements of the upconverter solar cell device using the BaY2F8:30% Er3+ sample showed an additional short-circuit current density due to upconversion ΔjSC,UC of 17.2±3.0 mA/cm2 at an illumination with a solar concentration of 94±17 suns, equivalent to a record relative enhancement of the short-circuit current of 0.55±0.14%. This value constitutes to our knowledge more than a doubling compared to the previously highest published values and more than a 35-fold increase compared to values published three years ago.
2015
S., Fischer; E., Favilla; Tonelli, Mauro; J. C., Goldschmidt
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11568/761946
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 95
  • ???jsp.display-item.citation.isi??? 88
social impact