In order to improve the thermal stability of PLA based materials the strategy of blending it with poly(carbonate) of bisphenol A (PC), having a higher glass transition temperature, was followed and PLA/PC blends with different compositions, obtained also in the presence of an interchange reaction catalyst, Tetrabutylammonium tetraphenylborate (TBATPB) and triacetin were prepared by melt extrusion. The dynamical mechanical characterization showed an interesting change of the storage modulus behavior in the PLA glass transition region, evident exclusively in the catalyzed blends. In particular, a new peak in the Tanδ trend at a temperature in between the one of PLA and the one of PC was observed only in the blends obtained in the presence of triacetin and TBATPB. The height and maximum temperature of the peak was different after the annealing of samples at 80°C. The data, showing an interesting improvement of thermal stability above the PLA glass transition, were explained keeping into account the formation of PLA-PC copolymer during the reactive extrusion. Furthermore, the glass transition temperature of the copolymer as a function of composition was studied and the obtained trend was discussed by comparing with literature models developed for copolymers. © 2014 AIP Publishing LLC.

Modification of the mechanical behavior in the glass transition region of poly(lactic acid) (PLA) through catalyzed reactive extrusion with poly(carbonate) (PC)

Phuong, Vu Thanh
Primo
Investigation
;
Coltelli, Maria-Beatrice
Secondo
Writing – Original Draft Preparation
;
Anguillesi, Irene
Methodology
;
Cinelli, Patrizia
Penultimo
Supervision
;
Lazzeri, Andrea
Ultimo
Supervision
2014-01-01

Abstract

In order to improve the thermal stability of PLA based materials the strategy of blending it with poly(carbonate) of bisphenol A (PC), having a higher glass transition temperature, was followed and PLA/PC blends with different compositions, obtained also in the presence of an interchange reaction catalyst, Tetrabutylammonium tetraphenylborate (TBATPB) and triacetin were prepared by melt extrusion. The dynamical mechanical characterization showed an interesting change of the storage modulus behavior in the PLA glass transition region, evident exclusively in the catalyzed blends. In particular, a new peak in the Tanδ trend at a temperature in between the one of PLA and the one of PC was observed only in the blends obtained in the presence of triacetin and TBATPB. The height and maximum temperature of the peak was different after the annealing of samples at 80°C. The data, showing an interesting improvement of thermal stability above the PLA glass transition, were explained keeping into account the formation of PLA-PC copolymer during the reactive extrusion. Furthermore, the glass transition temperature of the copolymer as a function of composition was studied and the obtained trend was discussed by comparing with literature models developed for copolymers. © 2014 AIP Publishing LLC.
2014
9780735412330
9780735412330
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11568/1141137
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 5
  • ???jsp.display-item.citation.isi??? ND
social impact