Pain is a prevalent problem that can raise morbidity of patients. Pain killer releasing biodegradable materials have been developed by using different techniques and biomaterials. The objective of the current study is to evaluate the use of a new bioerodible polymer for release of diclofenac sodium (DS). 1-butanol hemiester poly(maleic anhydride-alt-2-methoxyethyl vinyl ether) (PAM14) was prepared in the university of Pisa and selected as polymer of choice for the study. Polymer solutions of 5-10% (in ethanol or in acetic acid) were prepared, half of them containing 2% DS. The solutions were then electrospun to produce nanomats that were subsequently characterized using SEM. Fiber diameter was 160 nm 1 μm. Increasing polymer concentration increased the size of the fibers but reduced the number of beads (with or without DS). In the specimens obtained from acetic acid solution, the addition of DS resulted in a reduction in fiber diameter and an increase in the inter-bead distance. Corresponding ethanol solutions gave more homogeneous specimens than did acetic acid, having a lower number of beads. With the addition of DS a reduction in fiber diameter was observed for the acetic acid specimens. However, in ethanol, adding DS resulted in increased fiber diameter. Accordingly, it can be concluded that it is feasible to develop electrospun diclofenac releasing bioerodible nanostructures that have potential use in pain management. Their further evaluation is however, needed both in vitro and in vivo. © 2008 American Institute of Physics.

Diclofenac sodium (DS) loaded bioerodible polymer based constructs

PIRAS, ANNA MARIA;CHIELLINI, FEDERICA;CHIELLINI, EMO
2008-01-01

Abstract

Pain is a prevalent problem that can raise morbidity of patients. Pain killer releasing biodegradable materials have been developed by using different techniques and biomaterials. The objective of the current study is to evaluate the use of a new bioerodible polymer for release of diclofenac sodium (DS). 1-butanol hemiester poly(maleic anhydride-alt-2-methoxyethyl vinyl ether) (PAM14) was prepared in the university of Pisa and selected as polymer of choice for the study. Polymer solutions of 5-10% (in ethanol or in acetic acid) were prepared, half of them containing 2% DS. The solutions were then electrospun to produce nanomats that were subsequently characterized using SEM. Fiber diameter was 160 nm 1 μm. Increasing polymer concentration increased the size of the fibers but reduced the number of beads (with or without DS). In the specimens obtained from acetic acid solution, the addition of DS resulted in a reduction in fiber diameter and an increase in the inter-bead distance. Corresponding ethanol solutions gave more homogeneous specimens than did acetic acid, having a lower number of beads. With the addition of DS a reduction in fiber diameter was observed for the acetic acid specimens. However, in ethanol, adding DS resulted in increased fiber diameter. Accordingly, it can be concluded that it is feasible to develop electrospun diclofenac releasing bioerodible nanostructures that have potential use in pain management. Their further evaluation is however, needed both in vitro and in vivo. © 2008 American Institute of Physics.
2008
9780735404922
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11568/814360
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 0
  • ???jsp.display-item.citation.isi??? 0
social impact