A redox active Ni-Pd alloy nanocluster [Ni22-xPd20+x(CO)48]6-(x= 0.62) ([>1>]6-) was obtained from the redox condensation of [NBu4]2[Ni6(CO)12] with 0.7-0.8 equivalents of Pd(Et2S)2Cl2in CH2Cl2. Conversely, [Ni29-xPd6+x(CO)42]6-(x= 0.09) ([>2>]6-) and [Ni29+xPd6-x(CO)42]6-(x= 0.27) ([>3>]6-) were obtained by employing [NEt4]2[Ni6(CO)12] and 0.6-0.7 equivalents of Pd(Et2S)2Cl2in CH3CN. The molecular structures of these high nuclearity Ni-Pd carbonyl clusters were determined by single-crystal X-ray diffraction (SC-XRD). [>1>]6-adopted an M40ccpstructure comprising five close-packed ABCAB layers capped by two additional Ni atoms. Conversely, [>2>]6-and [>3>]6-displayed anhcpM35metal core composed of three compact ABA layers. [>1>]6-, [>2>]6-and [>3>]6-showed nanometric sizes, with the maximum lengths of their metal cores being 1.3 nm ([>1>]6-) and 1.0 nm ([>2>]6-and [>3>]6-), which increased up to 1.9 and 1.5 nm, after including also the CO ligands. Ni-Pd distribution within their metal cores was achieved by avoiding terminal Pd-CO bonding and minimizing Pd-CO coordination. As a consequence, site preference and partial metal segregation were observed, as well as some substitutional and compositional disorders. Electrochemical and spectroelectrochemical studies revealed that [>1>]6-and [>2>]6-were redox active and displayed four and three stable oxidation states, respectively. Even though several redox active high nuclearity metal carbonyl clusters have been previously reported, the nanoclusters described herein represent the first examples of redox active Ni-Pd carbonyl alloy nanoclusters.

Redox active Ni-Pd carbonyl alloy nanoclusters: syntheses, molecular structures and electrochemistry of [Ni22-xPd20+x(CO)48]6-(x= 0.62), [Ni29-xPd6+x(CO)42]6-(x= 0.09) and [Ni29+xPd6-x(CO)42]6-(x= 0.27)

Funaioli T.;
2020-01-01

Abstract

A redox active Ni-Pd alloy nanocluster [Ni22-xPd20+x(CO)48]6-(x= 0.62) ([>1>]6-) was obtained from the redox condensation of [NBu4]2[Ni6(CO)12] with 0.7-0.8 equivalents of Pd(Et2S)2Cl2in CH2Cl2. Conversely, [Ni29-xPd6+x(CO)42]6-(x= 0.09) ([>2>]6-) and [Ni29+xPd6-x(CO)42]6-(x= 0.27) ([>3>]6-) were obtained by employing [NEt4]2[Ni6(CO)12] and 0.6-0.7 equivalents of Pd(Et2S)2Cl2in CH3CN. The molecular structures of these high nuclearity Ni-Pd carbonyl clusters were determined by single-crystal X-ray diffraction (SC-XRD). [>1>]6-adopted an M40ccpstructure comprising five close-packed ABCAB layers capped by two additional Ni atoms. Conversely, [>2>]6-and [>3>]6-displayed anhcpM35metal core composed of three compact ABA layers. [>1>]6-, [>2>]6-and [>3>]6-showed nanometric sizes, with the maximum lengths of their metal cores being 1.3 nm ([>1>]6-) and 1.0 nm ([>2>]6-and [>3>]6-), which increased up to 1.9 and 1.5 nm, after including also the CO ligands. Ni-Pd distribution within their metal cores was achieved by avoiding terminal Pd-CO bonding and minimizing Pd-CO coordination. As a consequence, site preference and partial metal segregation were observed, as well as some substitutional and compositional disorders. Electrochemical and spectroelectrochemical studies revealed that [>1>]6-and [>2>]6-were redox active and displayed four and three stable oxidation states, respectively. Even though several redox active high nuclearity metal carbonyl clusters have been previously reported, the nanoclusters described herein represent the first examples of redox active Ni-Pd carbonyl alloy nanoclusters.
2020
Berti, B.; Cesari, C.; Femoni, C.; Funaioli, T.; Iapalucci, M. C.; Zacchini, S.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11568/1064797
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? 4
  • Scopus 12
  • ???jsp.display-item.citation.isi??? 9
social impact