In this study, the low temperature creep properties of multiphase bituminous materials (binder, mastic, Fine Aggregate Matrix - FAM, and mixture) were experimentally evaluated, and the impact of size effect on FAM and mixture specimen was also assessed. First, the mix design of mastic and FAM were performed based on the reference mixture AC 22 TS. The mathematical adaptation to the boundary sieve method was applied to calculate FAM gradation and binder content. Next, a preparation method was proposed to produce Fine Aggregate Matrix (FAM) in a laboratory environment, and scale-up slab samples were also fabricated for FAM and mixture specimens to evaluate the size effect phenomenon. Finally, three-point bending (3PB) creep tests were conducted on the multiphase bituminous specimens with different dimensions at -6°C, -12°C, and − 18°C with a modified Bending Beam Rheometer (BBR) device and a dynamic loading machine, depending on the sample size. Results indicate that the creep stiffness of the FAM was close to mixtures and much higher than the one observed in binder and mastic. The proposed fabrication approach provides a satisfactory method for preparing a representative FAM phase in the mixture, while the air voids can be easily adjusted during the slab compaction procedure. This study supports the idea of using FAM to discriminate asphalt mixtures for cold regions. The correlation between up-scaled FAM and mixtures specimens is recommended to be further investigated, including different mixture types and corresponding FAM.
Fabrication and characterization of multiphase bituminous materials for cold region pavements
Riccardi, ChiaraPenultimo
Formal Analysis
;
2023-01-01
Abstract
In this study, the low temperature creep properties of multiphase bituminous materials (binder, mastic, Fine Aggregate Matrix - FAM, and mixture) were experimentally evaluated, and the impact of size effect on FAM and mixture specimen was also assessed. First, the mix design of mastic and FAM were performed based on the reference mixture AC 22 TS. The mathematical adaptation to the boundary sieve method was applied to calculate FAM gradation and binder content. Next, a preparation method was proposed to produce Fine Aggregate Matrix (FAM) in a laboratory environment, and scale-up slab samples were also fabricated for FAM and mixture specimens to evaluate the size effect phenomenon. Finally, three-point bending (3PB) creep tests were conducted on the multiphase bituminous specimens with different dimensions at -6°C, -12°C, and − 18°C with a modified Bending Beam Rheometer (BBR) device and a dynamic loading machine, depending on the sample size. Results indicate that the creep stiffness of the FAM was close to mixtures and much higher than the one observed in binder and mastic. The proposed fabrication approach provides a satisfactory method for preparing a representative FAM phase in the mixture, while the air voids can be easily adjusted during the slab compaction procedure. This study supports the idea of using FAM to discriminate asphalt mixtures for cold regions. The correlation between up-scaled FAM and mixtures specimens is recommended to be further investigated, including different mixture types and corresponding FAM.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.