In this study, the fatigue strength of polished drill pipe specimens was investigated and compared with previous test results of corroded and not-corroded pipes. The resonant fatigue test rig, which was designed and implemented by the University of Pisa, is initially presented by providing a detailed description of the set-up of the machine, the calibration of the strain gauges, the control system, and the correct identification of the vibrational node locations. A polishing rig was also designed and put into operation to remove the corrosion pits from the outer surface of almost the entire length of the drill pipe specimens. After the fatigue tests with the resonant rig, and the observation of the fatigue fracture of the specimens, a few samples were extracted from different zones (corroded and not corroded) of the failed drill pipe specimens. This allowed for investigations to be carried out using a scanning electronic microscope. The obtained results were analyzed using the Murakami model, and a discussion is presented about the effect of the corrosion pits on the fatigue strength.

Resonant Fatigue Tests on Polished Drill Pipe Specimens

Ciro Santus
Primo
;
Lorenzo Romanelli
;
Leonardo Bertini;
2024-01-01

Abstract

In this study, the fatigue strength of polished drill pipe specimens was investigated and compared with previous test results of corroded and not-corroded pipes. The resonant fatigue test rig, which was designed and implemented by the University of Pisa, is initially presented by providing a detailed description of the set-up of the machine, the calibration of the strain gauges, the control system, and the correct identification of the vibrational node locations. A polishing rig was also designed and put into operation to remove the corrosion pits from the outer surface of almost the entire length of the drill pipe specimens. After the fatigue tests with the resonant rig, and the observation of the fatigue fracture of the specimens, a few samples were extracted from different zones (corroded and not corroded) of the failed drill pipe specimens. This allowed for investigations to be carried out using a scanning electronic microscope. The obtained results were analyzed using the Murakami model, and a discussion is presented about the effect of the corrosion pits on the fatigue strength.
2024
Santus, Ciro; Romanelli, Lorenzo; Bertini, Leonardo; Burchianti, Alessandro; Inoue, Tomoya
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11568/1232827
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact