Spectroscopic properties of neodymium-doped yttrium orthovanadate crystals were measured in the temperature range between 5 and 350 K. Crystals fabricated by different suppliers, with 0.3 and 1 at% Nd(3+), were compared. For each temperature, the stimulated emission cross sections of the Nd(3+) (4)F(3/2) decay to the (4)I(9/2), (4)I(1/2), and (4)I(13/2) states were obtained using the Fuchtbauer-Ladenburg and the reciprocity techniques. Nd:YVO(4) shows higher absorption at room temperature and higher stimulated emission cross section with similar variation with temperature when compared with Nd:YAG. The anomalous dependence on temperature of the Nd(3+) (4)F(3/2) excited-state lifetime is discussed and an explanation is suggested. (C) 2009 Optical Society of America

Temperature-dependent stimulated emission cross section in Nd(3+) : YVO(4) crystals

TONELLI, MAURO;
2009-01-01

Abstract

Spectroscopic properties of neodymium-doped yttrium orthovanadate crystals were measured in the temperature range between 5 and 350 K. Crystals fabricated by different suppliers, with 0.3 and 1 at% Nd(3+), were compared. For each temperature, the stimulated emission cross sections of the Nd(3+) (4)F(3/2) decay to the (4)I(9/2), (4)I(1/2), and (4)I(13/2) states were obtained using the Fuchtbauer-Ladenburg and the reciprocity techniques. Nd:YVO(4) shows higher absorption at room temperature and higher stimulated emission cross section with similar variation with temperature when compared with Nd:YAG. The anomalous dependence on temperature of the Nd(3+) (4)F(3/2) excited-state lifetime is discussed and an explanation is suggested. (C) 2009 Optical Society of America
2009
Turri, Giorgio; Jenssen Hans, P.; Cornacchia, Francesco; Tonelli, Mauro; Bassi, Michael
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11568/129982
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact