The phenomenology of the a relaxation process in an amorphous and crystallized specimen of a side-chain LC polyacrylate, based on the azobenzene mesogenic unit, was investigated by thermal and dynamic-mechanical methods. A frequency and temperature analysis was performed. The relaxation behavior of the amorphous sample was described by the WLF equation. The alpha process of the semicrystalline sample was structured into two components alpha' and alpha '', both following Arrhenius type activation law. This peculiar behavior has been tentatively related to the multidomain structure of the semicrystalline sample.
On the peculiar dynamic-mechanical behavior of an azobenzene-containing mesomorphic polyacrylate
CHIELLINI, EMO;ANDREOZZI, LAURA;LEPORINI, DINO
1995-01-01
Abstract
The phenomenology of the a relaxation process in an amorphous and crystallized specimen of a side-chain LC polyacrylate, based on the azobenzene mesogenic unit, was investigated by thermal and dynamic-mechanical methods. A frequency and temperature analysis was performed. The relaxation behavior of the amorphous sample was described by the WLF equation. The alpha process of the semicrystalline sample was structured into two components alpha' and alpha '', both following Arrhenius type activation law. This peculiar behavior has been tentatively related to the multidomain structure of the semicrystalline sample.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.