Biocompatible polymers with specific shape and tailored hydrogel properties were obtained by polymerization of mixtures of 2-hydroxyethyl methacrylate (HEMA) with 1-8 wt %, ethylene glycol dimethacrylate (EGDMA) or tetra(ethylene glycol) diacrylate (TEGDA) as crosslinking agents, by using a redox initiator. Introduction of charged positive and negative groups was easily achieved by direct polymerization of appropriate monomer mixtures and by chemical transformation of preformed hydrogels. Investigation of the swelling behavior of the prepared hydrogels evidenced an appreciable dependence on both solvent type and polymer chemical structure. Additionally, the solvation process resulted in being controlled by solvent diffusion, according to a Fickian II mechanism. The presence of several types of water with different melting behavior was observed in fully swollen hydrogels
Bioerodible hydrogels based on 2-hydroxyethyl methacrylate: synthesis and characterization
CHIELLINI, FEDERICA;SOLARO, ROBERTO
2002-01-01
Abstract
Biocompatible polymers with specific shape and tailored hydrogel properties were obtained by polymerization of mixtures of 2-hydroxyethyl methacrylate (HEMA) with 1-8 wt %, ethylene glycol dimethacrylate (EGDMA) or tetra(ethylene glycol) diacrylate (TEGDA) as crosslinking agents, by using a redox initiator. Introduction of charged positive and negative groups was easily achieved by direct polymerization of appropriate monomer mixtures and by chemical transformation of preformed hydrogels. Investigation of the swelling behavior of the prepared hydrogels evidenced an appreciable dependence on both solvent type and polymer chemical structure. Additionally, the solvation process resulted in being controlled by solvent diffusion, according to a Fickian II mechanism. The presence of several types of water with different melting behavior was observed in fully swollen hydrogelsI documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.