This work deals with the experimental evaluation of the thermal conductivity of a concrete matrix to be used for embedding LILW bituminised Wastes into the packaging system. Such a type of packaging, identified with the acronym CP5.2, has been also qualified by executing at the Lab. Scalbatraio of Dep. of Civil and Industrial Engineering of the University of Pisa, an experimental test campaign accordingly to the IAEA regulations. In particular, the knowledge of the thermal conductivity is important because of the fire or furnace test to carry out in oven at 800 °C for 30 minutes. These data allowed to simulate pre-test conditions and to set up safety and operational fire test procedures. The concrete thermal conductivity was obtained by performing hot wire tests on cylindrical concrete samples for temperatures ranging from 100° to about 800°C. Thermal conductivity is determined at steady state condition. Results indicate a monotonically reduction of the thermal conductivity as the temperature increases. The comparison with concrete thermal conductivity data available in literature indicates a quite good agreement. Finally, visual and X-ray inspection of sample did not highlight the presence of micro/macro damages that would have affected the thermal performance of the concrete under study.
Experimental thermal characterization of concrete to be used in CP5.2 packaging system
LO FRANO, ROSA;AQUARO, DONATO
2016-01-01
Abstract
This work deals with the experimental evaluation of the thermal conductivity of a concrete matrix to be used for embedding LILW bituminised Wastes into the packaging system. Such a type of packaging, identified with the acronym CP5.2, has been also qualified by executing at the Lab. Scalbatraio of Dep. of Civil and Industrial Engineering of the University of Pisa, an experimental test campaign accordingly to the IAEA regulations. In particular, the knowledge of the thermal conductivity is important because of the fire or furnace test to carry out in oven at 800 °C for 30 minutes. These data allowed to simulate pre-test conditions and to set up safety and operational fire test procedures. The concrete thermal conductivity was obtained by performing hot wire tests on cylindrical concrete samples for temperatures ranging from 100° to about 800°C. Thermal conductivity is determined at steady state condition. Results indicate a monotonically reduction of the thermal conductivity as the temperature increases. The comparison with concrete thermal conductivity data available in literature indicates a quite good agreement. Finally, visual and X-ray inspection of sample did not highlight the presence of micro/macro damages that would have affected the thermal performance of the concrete under study.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.