A wide range of poly(hydroxyalkanoate)s (PHAs), a class of biodegradable polyesters produced by various bacteria grown under unbalanced conditions, have been proposed for the fabrication of tissue-engineering scaffolds. In this study, the manufacture of poly[(R)-3-hydroxybutyrate-co-(R)-3-hydroxyhexanoate] (or PHBHHx) scaffolds, by means of an additive manufacturing technique based on a computer-controlled wet-spinning system, was investigated. By optimizing the processing parameters, three-dimensional scaffolds with different internal architectures were fabricated, based on a layer-by-layer approach. The resulting scaffolds were characterized by scanning electron microscopy, which showed good control over the fibre alignment and a fully interconnected porous network, with porosity in the range 79–88%, fibre diameter 47–76 µm and pore size 123–789 µm. Moreover, the resulting fibres presented an internal porosity connected to the external fibre surface as a consequence of the phase-inversion process governing the solidification of the polymer solution. Scaffold compressive modulus and yield stress and strain could be varied in a certain range by changing the architectural parameters. Cell-culture experiments employing the MC3T3-E1 murine pre-osteoblast cell line showed good cell proliferation after 21 days of culture. The PHBHHx scaffolds demonstrated promising results in terms of cell differentiation towards an osteoblast phenotype. Copyright © 2014 John Wiley & Sons, Ltd.

Additive manufacturing of poly[(R)-3-hydroxybutyrate-co-(R)-3-hydroxyhexanoate] scaffolds for engineered bone development

PUPPI, DARIO;GAZZARRI, MATTEO;MIGONE, CHIARA;CHIELLINI, FEDERICA;
2017-01-01

Abstract

A wide range of poly(hydroxyalkanoate)s (PHAs), a class of biodegradable polyesters produced by various bacteria grown under unbalanced conditions, have been proposed for the fabrication of tissue-engineering scaffolds. In this study, the manufacture of poly[(R)-3-hydroxybutyrate-co-(R)-3-hydroxyhexanoate] (or PHBHHx) scaffolds, by means of an additive manufacturing technique based on a computer-controlled wet-spinning system, was investigated. By optimizing the processing parameters, three-dimensional scaffolds with different internal architectures were fabricated, based on a layer-by-layer approach. The resulting scaffolds were characterized by scanning electron microscopy, which showed good control over the fibre alignment and a fully interconnected porous network, with porosity in the range 79–88%, fibre diameter 47–76 µm and pore size 123–789 µm. Moreover, the resulting fibres presented an internal porosity connected to the external fibre surface as a consequence of the phase-inversion process governing the solidification of the polymer solution. Scaffold compressive modulus and yield stress and strain could be varied in a certain range by changing the architectural parameters. Cell-culture experiments employing the MC3T3-E1 murine pre-osteoblast cell line showed good cell proliferation after 21 days of culture. The PHBHHx scaffolds demonstrated promising results in terms of cell differentiation towards an osteoblast phenotype. Copyright © 2014 John Wiley & Sons, Ltd.
2017
Mota, Carlos; Wang, Shen Yu; Puppi, Dario; Gazzarri, Matteo; Migone, Chiara; Chiellini, Federica; Chen, Guo Qiang; Chiellini, Emo
File in questo prodotto:
File Dimensione Formato  
Post Print Manuscript PHBHHx_E Chiellini.pdf

accesso aperto

Descrizione: Articolo Principale
Tipologia: Documento in Post-print
Licenza: Tutti i diritti riservati (All rights reserved)
Dimensione 1.01 MB
Formato Adobe PDF
1.01 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11568/851325
Citazioni
  • ???jsp.display-item.citation.pmc??? 8
  • Scopus 58
  • ???jsp.display-item.citation.isi??? 48
social impact