Composite Nafion membranes containing three natural zeolites (Mordenite, Chabazite and Clinoptilolite) were prepared by using a recast procedure for application in high temperature Direct Methanol Fuel Cells (DMFCs). The Nafion-zeolite membranes have shown good properties for high temperature DMFC application, due to their improved water retention characteristics. A maximum power density of 390 mW cm)2 was achieved at 140 °C with the mordenite-based composite membranes in the presence of oxygen feed. The electrochemical behaviour of the composite membranes was interpreted in the light of surface properties and acidic characteristics of the fillers.
|Autori:||V. BAGLIO; A.S. ARICO; A. DI BLASI; P.L. ANTONUCCI; F. NANNETTI; V. TRICOLI; V. ANTONUCCI|
|Titolo:||Zeolite-based composite membranes for high temperature direct methanol fuel cells|
|Anno del prodotto:||2005|
|Appare nelle tipologie:||1.1 Articolo in rivista|