A novel mixed zirconium phosphate/phosphonate based on glyphosine, of formula Zr2(PO4)H5(L)2·H2O [L = (O3PCH2)2NCH2COO], was synthesized in mild conditions. The compound has a layered structure that was solved ab initio from laboratory PXRD data. It crystallizes in the monoclinic C2/c space group with the following cell parameters: a = 29.925(3), b = 8.4225(5), c = 9.0985(4) Å, and β = 98.474(6)°. Phosphate groups are placed inside the sheets and connect the zirconium atoms in a tetradentate fashion, while uncoordinated carboxylate and P-OH phosphonate groups are exposed on the layer surface. Due to the presence of these acidic groups, the compound showed remarkable proton conductivity properties, which were studied in a wide range of temperature and relative humidity (RH). The conductivity is strongly dependent on RH and reaches 1 × 10-3 S cm-1 at 140 °C and 95% RH. At this RH, the activation energy of conduction is 0.15 eV in the temperature range 80-140 °C. The similarities of this structure with related structures already reported in the literature were also discussed.

A layered mixed zirconium phosphate/phosphonate with exposed carboxylic and phosphonic groups: X-ray powder structure and proton conductivity properties

Taddei M.;
2014-01-01

Abstract

A novel mixed zirconium phosphate/phosphonate based on glyphosine, of formula Zr2(PO4)H5(L)2·H2O [L = (O3PCH2)2NCH2COO], was synthesized in mild conditions. The compound has a layered structure that was solved ab initio from laboratory PXRD data. It crystallizes in the monoclinic C2/c space group with the following cell parameters: a = 29.925(3), b = 8.4225(5), c = 9.0985(4) Å, and β = 98.474(6)°. Phosphate groups are placed inside the sheets and connect the zirconium atoms in a tetradentate fashion, while uncoordinated carboxylate and P-OH phosphonate groups are exposed on the layer surface. Due to the presence of these acidic groups, the compound showed remarkable proton conductivity properties, which were studied in a wide range of temperature and relative humidity (RH). The conductivity is strongly dependent on RH and reaches 1 × 10-3 S cm-1 at 140 °C and 95% RH. At this RH, the activation energy of conduction is 0.15 eV in the temperature range 80-140 °C. The similarities of this structure with related structures already reported in the literature were also discussed.
2014
Donnadio, A.; Nocchetti, M.; Costantino, F.; Taddei, M.; Casciola, M.; Da Silva Lisboa, F.; Vivani, R.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11568/1024443
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? 5
  • Scopus 66
  • ???jsp.display-item.citation.isi??? 64
social impact