Bioartificial blends of poly-(ε-caprolactone) (PCL) with a polysaccharide (starch, S; dextran, D; or gellan, G) (PCL/S, PCL/D, PCL/G 90.9/9.1 wt ratio) were prepared by a solution−precipitation technique and widely characterized by differential scanning calorimetry analysis (DSC), Fourier transform infrared-attenuated total reflectance spectroscopy (FTIR-ATR), optical microscopy (OM), wide-angle X-ray diffraction analysis (WAXD), and thermogravimetry (TGA). DSC showed that the polysaccharide reduced the crystallinity of PCL and had a nucleation effect, which was also confirmed by OM analysis. Hoffman−Weeks analysis was performed on PCL and blend samples allowing calculation of their equilibrium melting temperatures ( ). WAXD showed that the crystalline unit cell type was the same for PCL and blends. FTIR-ATR did not evidence interactions between blend components. Thermal stability was affected by the type of polysaccharide. Microparticles (<125 μm) were produced from blends by cryogenical milling and characterized by scanning electron microscopy analysis (SEM). Selective laser sintering (SLS), a new rapid prototyping technology for scaffold fabrication, was applied to sinter blend microparticles according to a PC-designed two-dimensional geometry (strips and 2 × 2 mm2 square-meshed grids). The optimal experimental conditions for sintering were established and laser beam parameters (beam speed, BS, and power, P) were found for each blend composition. Morphology of sintered objects was analyzed by SEM and found to be dependent on the morphology of the sintered powders. Sintered samples were analyzed by chemical imaging (CI), FTIR-ATR, DSC, and contact angle analysis. No evidence of the occurrence of degradation phenomena was found by FTIR-ATR for sintered samples, whereas DSC parameters of PCL and blends showed changes which could be attributed to some molecular weight decrease of PCL during sintering. CI of sintered samples showed that the polysaccharide phase was homogeneously dispersed within the PCL matrix, with the only exception being the PCL/D blend. The contact angle analysis showed that all samples were hydrophilic. Fibroblasts were then seeded on scaffolds to evaluate the rate and the extent of cell adhesion and the effect of the polysaccharides (S, D, G) on the bioactivity of the PCL-based blends.

Blends of poly-(epsilon-caprolactone) and polysaccharides in tissue engineering applications

VOZZI, GIOVANNI;AHLUWALIA, ARTI DEVI;BARBANI, NICCOLETTA;PRACELLA, MARIANO;GIUSTI, PAOLO
2005-01-01

Abstract

Bioartificial blends of poly-(ε-caprolactone) (PCL) with a polysaccharide (starch, S; dextran, D; or gellan, G) (PCL/S, PCL/D, PCL/G 90.9/9.1 wt ratio) were prepared by a solution−precipitation technique and widely characterized by differential scanning calorimetry analysis (DSC), Fourier transform infrared-attenuated total reflectance spectroscopy (FTIR-ATR), optical microscopy (OM), wide-angle X-ray diffraction analysis (WAXD), and thermogravimetry (TGA). DSC showed that the polysaccharide reduced the crystallinity of PCL and had a nucleation effect, which was also confirmed by OM analysis. Hoffman−Weeks analysis was performed on PCL and blend samples allowing calculation of their equilibrium melting temperatures ( ). WAXD showed that the crystalline unit cell type was the same for PCL and blends. FTIR-ATR did not evidence interactions between blend components. Thermal stability was affected by the type of polysaccharide. Microparticles (<125 μm) were produced from blends by cryogenical milling and characterized by scanning electron microscopy analysis (SEM). Selective laser sintering (SLS), a new rapid prototyping technology for scaffold fabrication, was applied to sinter blend microparticles according to a PC-designed two-dimensional geometry (strips and 2 × 2 mm2 square-meshed grids). The optimal experimental conditions for sintering were established and laser beam parameters (beam speed, BS, and power, P) were found for each blend composition. Morphology of sintered objects was analyzed by SEM and found to be dependent on the morphology of the sintered powders. Sintered samples were analyzed by chemical imaging (CI), FTIR-ATR, DSC, and contact angle analysis. No evidence of the occurrence of degradation phenomena was found by FTIR-ATR for sintered samples, whereas DSC parameters of PCL and blends showed changes which could be attributed to some molecular weight decrease of PCL during sintering. CI of sintered samples showed that the polysaccharide phase was homogeneously dispersed within the PCL matrix, with the only exception being the PCL/D blend. The contact angle analysis showed that all samples were hydrophilic. Fibroblasts were then seeded on scaffolds to evaluate the rate and the extent of cell adhesion and the effect of the polysaccharides (S, D, G) on the bioactivity of the PCL-based blends.
2005
Ciardelli, G.; Chiono, V.; Vozzi, Giovanni; Ahluwalia, ARTI DEVI; Barbani, Niccoletta; Cristallini, C.; Pracella, Mariano; Giusti, Paolo
File in questo prodotto:
File Dimensione Formato  
Arpi 206303.pdf

solo utenti autorizzati

Tipologia: Versione finale editoriale
Licenza: NON PUBBLICO - Accesso privato/ristretto
Dimensione 2.36 MB
Formato Adobe PDF
2.36 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11568/206303
Citazioni
  • ???jsp.display-item.citation.pmc??? 31
  • Scopus 305
  • ???jsp.display-item.citation.isi??? 263
social impact