Dielectric Response of a Conducting Polymer Dominated by the Hopping Charge Transport

The d.c. conductivity and the electric a.c, response from 100 Hz up to 40 MHz of poly(3n-decylpyrrole) were measured in the 80-330 K interval to characterize the charge transport behaviour of the system. The d.c. conductivity well fitted the variable range hopping model, and the loss factor. after having deducted the d.c. contribution showed a relaxation peak when the conductivity versus frequency started to rise. The strength of this relaxation increased with temperature and became too large to be related to a dipolar relaxation; moreover, the temperature dependence of the loss peak frequency and d.c. conductivity coincided. The observed relaxation was attributed to the hopping charge transport, as further confirmed by the temperature behaviour of the relaxation strength and by the frequency dependence of the exponents of the power law which locally approximate the conductivity behaviour. As the activation energy of the d.c. conductivity differed from the frequency of the loss peak, the theoretical prediction concerning the selfsimilarity of the a.c, conductivity was roughly verified.